Industrial sponge roller device having reduced residuals

ABSTRACT

An industrial sponge device and a method of manufacturing the same. The sponge is made from a polyvinyl acetal material with a process in which the pores are formed by gas to provide an open pore structure having no fibrils. Additionally, the sponge is purified by an extracting process which includes alternating exposure of the partially cross-linked sponge to solutions of high pH and low pH. The sponge is sterilized by electron beam radiation to destroy micro organisms that can cause contamination of the final product. The resulting sponge material is formed into an industrial sponge having a cylindrical body and a plurality of projections extending from the body. The projections are tapered truncated cones having a cross-sectional radius that decreases with distance from the body. The extracting process permits residual amounts of calcium, zinc, and other elements to be 2 ppm or less. preferably 1 ppm or less.

CROSS-REFERENCE TO RELATED PATENT APPLICATIONS

[0001] This application is a continuation-in-part of U.S. patent application Ser. No. 08/780,895 filed on Jan. 9, 1997 which is a continuation-in-part of U.S. patent application Ser. No. 08/319,005 filed on Oct. 6, 1994, the disclosures of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

[0002] 1. Field of the Invention

[0003] The present invention relates to an industrial sponge used for cleaning surfaces. More specifically, the invention is a synthetic industrial sponge made of polyvinyl acetal, and a method for extracting residue from the sponge to yield a sponge that leaves less particulate matter and has a longer life than conventional sponges, and a method of cleaning semiconductor material using the sponges.

[0004] 2. Description of the Related Art

[0005] The use of synthetic sponges, made of polyvinyl acetal for example, is well known. For example, U.S. Pat. No. 4,566,911 discloses a scrubbing device using a polyvinyl acetal elastic material. Conventional sponges have been shaped in various forms, such as rollers and pads. These sponges are used to clean critical materials such as thin film disks, semiconductor wafers, data storage media, and other materials requiring removal of particles in the 0.1 micron range, i.e. “ultimate cleaning”. Conventional synthetic sponges have a polymer structure with “dead end pockets” formed therein that trap residue and trace amounts of metals. As the sponge wears, these metals can come out of the sponge in the form of particulate matter. Such particulate matter can damage the surfaces that are to be cleaned. Further, this type of sponge has tiny fibrils in the pores thereof that are a result of spaces between the pore forming chemical additive during a cross-linking reaction. “Cross-linking” is the formation of ester bonding between chains of the two adjacent hydroxyl groups that occur with the reaction of polyvinyl alcohol and aldehyde. This reaction hardens and strengthens the resulting material.

[0006] U.S. Pat. No. 4,098,728, the disclosure of which is incorporated herein by reference, discloses a polyvinyl acetal sponge and a method for making the same. In this method, pore spaces in the sponge are formed by gas bubbles; not pore forming chemical additives such as starch/sulfate combinations. Because the sponge disclosed in this patent does not have any starch residue, or the like, it has been particularly useful in medical applications in which starch residues can cause a foreign body reaction when in contact with mucosal tissue.

[0007] Also, conventional sponges have been used to form cleaning rollers or the like having projections formed on a surface thereof. However, the conventional projections have walls that extend perpendicular to an outer surface of the sponge body. Such a configuration creates stress concentration areas. Accordingly, the projections break off of the roller surface after continued use. Therefore, conventional sponges having projections have a short useful life.

[0008] Finally, extraction processes, also known as purification processes, are used to remove particulate matter and residue from the sponge before the sponge is used for cleaning. However, conventional extraction processes have not adequately removed residue to the extent necessary for reliably cleaning semiconductor wafers or similar materials.

SUMMARY OF THE INVENTION

[0009] It is an object of the invention to overcome the limitations of the prior art polyvinyl acetal sponges.

[0010] It is a further object of the invention to minimize particulate residue in a polyvinyl acetal sponge.

[0011] It is still a further object of the invention to extend the life of polyvinyl acetal sponges.

[0012] The invention achieves these objectives by forming a polyvinyl acetal sponge with a process in which the pores are formed by gas to provide an open pore structure having no fibrils. Additionally, the sponge is purified by alternating exposure of the partially cross-linked sponge to solutions of high pH and low pH. The sponge is sterilized by electron beam radiation to destroy micro organisms that can cause contamination of the final product. Residue in the sponge is reduced to 2 ppm or less, preferably 1 ppm or less for many elements, zinc and calcium in particular.

[0013] The resulting sponge material is formed into an industrial sponge having a cylindrical body and a plurality of projections extending from the body. The projections are tapered truncated cones having a cross-sectional radius that decreases with distance from the body. The projections of the invention provide increased contact pressure without reducing the life of the industrial sponge to unacceptable levels. The sponge material can be used for cleaning semiconductor wafers or other materials by rolling the sponge across a surface of the material in a known manner.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014]FIG. 1 is a perspective view of a sponge roller device according to a preferred embodiment of the invention;

[0015]FIG. 2 is a cross-sectional view along line 2′-2′ of FIG. 1;

[0016]FIG. 3 is a partial cross-sectional view taken along line 3′-3′ of FIG. 1;

[0017]FIG. 4 is a micro photograph of the sponge material of the preferred embodiment;

[0018]FIG. 5 is a microphotograph of a typical conventional sponge material;

[0019]FIG. 6 is a microphotograph of the conventional sponge illustrating residual starch particles; and

[0020]FIG. 7 is a microphotograph of the conventional sponge at 100× magnification illustrating the bi-refringent calorimetric method used to isolate the starch particles.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT

[0021] A preferred embodiment of the invention is illustrated in FIGS. 1-3. Applicant has discovered that the sponge making process disclosed in U.S. Pat. No. 4,098,728, the disclosure of which is incorporated herein by reference, can yield a sponge material having 100% open pores with no “dead end pockets” and no fibrils. Specifically, the sponge material is a continuous porous web interconnected material lacking fibrils that can result from spaces between pore forming chemicals during conventional cross-linking reactions. In conventional sponge materials, fibrils are formed as uncross-linked polymer flows into the spaces existing between and around the agglomerated solid particles of starch/sulfate or other pore forming chemicals. As the cross-linking reaction proceeds, small incursions into these spaces become solidified as fibrils. FIG. 4 is a microphotograph of the sponge material used to form sponge roller device 10. The sponge material is formed of interconnected thin-walled structures with holes of substantially circular or oval cross section. The pore geometry of the sponge material does not contain micro fibers, i.e. fibrils, on the walls that define the pores. Also, the pore walls are attached to each other by a web-like membrane which is itself porous. In contrast, FIG. 5 illustrates the material used in cleaning and polishing rolls manufactured by Kanebo Corporation and distributed in the U.S. by Rippey, which is a typical conventional polyvinyl acetal sponge material. This material clearly contains tiny fibrils that were created by pore forming chemicals during a cross-linking reaction. These fibrils can come loose and fall as particulate matter onto the device being cleaned thus reducing the cleaning efficiency of the resuting sponge.

[0022] The specific geometry of the pores is a function of the reaction parameters, such as temperature, mixing technique, pore forming method, cure time, reactant concentration, catalyst type and concentration, flow rates, and the like, as described in the above-noted patent. An example of the sponge material that can be used for the invention is the same as that used to form the readily available Merocel Sponge™ and Merocel PVA Roller Brushes™ sold by Merocel Corporation which is made by the process disclosed in the above-noted patent. Additionally, applicant's have found that known continuous mixing techniques can be used in place of the mixing technique disclosed in the patent.

[0023] As illustrated in FIG. 1, sponge roller device 10 is molded to form a cylindrical body having outer surface 12 and a plurality of truncated conical projections 14 extending from outer surface 12. Projections 14 are disposed at regular intervals in rows 30 and 32 that are offset from one another, in a direction along the longitudinal axis of the cylindrical body, to result in a staggered arrangement of projections 14 as is best illustrated in FIGS. 1 and 2. Preferably, projections 14 extend from outer surface 12 to a height of approximately 0.1875 inches as illustrated in FIG. 3. Also, projections 14 preferably are disposed at intervals to define an angle α of 22.5° between radial lines extending through the central axes of adjacent offset projections as shown in FIG. 2. Preferably, the diameter of base 18 is at least 20% larger than the diameter of top surface 16. The area of base 18 is preferably 40% larger than that of top surface 16.

[0024] Each projection 14 has planar top surface 16 that has a diameter of 0.25 inches and thus an area of 0.049 square inches. Also, each projection 14 has base 18 having a diameter of 0.31 inches and thus an area of 0.073 square inches. The taper of projection walls 19, which define the outer surface of the truncated cone, defines an angle β that is in the range of 5-20°, inclusive, and is preferably about 10° with respect to the central axis of the projection as shown in FIG. 3. This tapered wall configuration provides a base for the projection that is sufficiently large and prevents stress concentration points to prevent reduced life of sponge roller device 10 due to broken projections 14. Also, the tapered wall configuration permits foreign matter on the object to be cleaned to enter readily between projections 14 and retained between projections 14.

[0025] The sponge material is shaped into the sponge roller device 10 by a molding process. In particular, a polyethylene, ABS, or the like material is formed, through molding or the like, into a mold, i.e. a female version of the outer shape of the sponge roller device, with allowances for shrinkage, the amount of which can be determined experimentally. The mold can be made in separate segments and joined into one unit. The segments can be interlocked with one another and held together by end caps, or the like. The froth reactant of the sponge material is injected, or otherwise introduced, into the assembled mold and then the filled mold is placed in an insulated container where temperature is controlled during curing. This process is described in detail in U.S. Pat. No. 4,098,728.

[0026] The molded sponge material is then subjected to an extraction process to remove any trace amounts of metal and other residues that can cause particulate matter to fall out of the sponge material. The partially cross-linked, i.e 60% or less cross-linked, molded sponge roller is alternately exposed to solutions of high and low pH to precipitate metals from the pore spaces (high pH solutions) and dissolve trace amounts of metals (low pH solutions) from the pore spaces. Cross-linking in the range of 25-55% yields a strong, yet flexible sponge material.

[0027] A first preferred extraction method includes the following steps:

[0028] 1(a) soaking the rollers in water to dilute reactants and halt cross-linking, then washing rinsing and extracting the rollers until all acid catalyst is neutralized, i.e. a pH between 6.5 and 7.5 is reached; or

[0029] 1(b) soaking the rollers in water and then passing the rollers through rubber rolls or the like to compress the rollers and thus extract any solution therefrom;

[0030] 2) soaking the rollers in mineral acid at a concentration of 1 to 20% by weight (preferably between 1 and 5%) and washing and rinsing until all of the acid catalyst has been removed;

[0031] 3) oxidizing unreacted aldehydes that are within the pore structure to form carboxylic acids and neutralizing the acids to soluble salts and washing and rinsing to remove the salts, while raising the pH beyond 7.0 to precipitates metals;

[0032] 4) washing and rinsing to remove loosely held particulate matter;

[0033] 5) washing with deionized water, extracting and rinsing, the last rinse being with distilled water.

[0034] The steps above reduce extractable residue and particulate matter to very low levels (see the test results below) that are suitable for cleaning magnetic disk surfaces or the like. However, for cleaning silicon wafers, it is desirable that extractable residues of elements such as, calcium, zinc, arsenic, barium, cadmium, chloride, chromium, copper, iron, lead, manganese, magnesium, mercury, nitrate, potassium, selenium, silica, silver, and sodium each be reduced to 2 ppm. or less, preferably 1 ppm. or less. Also, it is desirable to reduce extractable sulfate to a value 10 ppm. or less. Reducing the values of extractable calcium and zinc is particularly important. Applicant has developed an additional second extraction process, to be conducted in seriatim with the first extraction process, that reduces extractable residue to these values. The second extraction process includes the following steps:

[0035] 1) high turbulence washing and rinsing and then centrifugal extraction to remove all liquid;

[0036] 2) exposure, through submersion or the like, to an acid solution of 0.1 to 10% (preferably 0.2 to 2.0%) of a mineral acid such as sulfuric acid for 1 to 90 hours (preferably 4 to 48 hours).

[0037] 3) more high turbulence washing and rinsing;

[0038] 4) oxidation of reactant aldehydes by soaking the rollers in an oxidizing bath up to 10% concentration within adjustment for pH between 7.5 and 11 (preferably between 8.0 and 9.5 in a hydrogen peroxide bath at 0.05% to 2.0% concentration) for to 96 hours (preferably 4 to 36 hours).

[0039] 5) repeat of steps 1-4 above until the pantanedione test, or a similar test, for alhehyde indicates less than 1.0 ppm HCO equivalent; and

[0040] 6) sterilization by electron beam radiation to destroy microorganisms, such as mold spores, which can contaminate the final product.

[0041] Steps 1-5 above reduce residue to a very low value. Step 6 eliminates the need for pesticide or other additives for sterilizing the roller. These additives require an expensive washout procedure and can further contribute to residue.

[0042]FIGS. 6 and 7 respectively illustrate residue (potato starch) remaining in the sponge material of the conventional sponge before use. The whitish spots in FIG. 6 are residue. FIG. 7 illustrates the bi-refringent calorimetric method used to isolate and detect the starch particles. Because the invention does not use starch to form pores, this residue is eliminated in the invention.

[0043] Comparative testing between the sponge material subjected to the extraction processes of the invention and the conventional sponge not subjected to the inventive extraction processes has been conducted. The first series of tests was a measure of extractible residue contained in the sponge material. The results of this test are illustrated in Tables 1-4 below. TABLE 1 (Invention Subjected to First Extraction Process Only): COMPONENT INVENTION COMPETITIVE SPONGE Calcium 2.6 ppm 2.6 ppm Chloride not detected 10 ppm Magnesium .17 ppm .22 ppm Potassium .21 ppm 6.3 ppm Nitrate 1.1 ppm 1.3 ppm Nitrite not detected not detected Silicon not detected not detected Sodium 3.4 ppm 5.8 ppm Total Non 36 ppm 39 ppm Volatile Residues

[0044] TABLE 2 (Invention Subjected to First and Second Extraction Process): COMPONENT INVENTION COMPETITIVE SPONGE Calcium 0.55 ppm 2.1 ppm Chloride Not Detectable 33.0 ppm Fluoride 0.98 ppm 125 ppm Magnesium 0.27 ppm 3.8 ppm Potassium 0.16 ppm 16.0 ppm Sodium 1.1 ppm 223 ppm Sulfate 5.4 ppm 79 ppm Zinc 0.07 ppm 4.5 ppm Total Non Not Detectable 308 ppm Volatile Residue

[0045] TABLE 3 (Invention Subjected to First and Second Extraction Processes): COMPONENT INVENTION COMPETITIVE SPONGE Calcium 0.2 ppm 2.60 ppm Potassium 0.03 ppm 6.30 ppm Nitrate 0.3 ppm 1.30 ppm Total Non Not Detectable 39.0 ppm Volatile Residues

[0046] TABLE 4 (Invention Subjected to First and Second Extraction Processes): COMPONENT INVENTION COMPETITIVE SPONGE Arsenic Not Detectable Not Detectable Barium Not Detectable Not Detectable Cadmium Not Detectable Not Detectable Calcium 0.2 ppm 1.6 ppm Chloride Not Detectable 57 ppm Chromium Not Detectable Not Detectable Copper Not Detectable 1.1 ppm Iron Not Detectable 1.6 ppm Lead Not Detectable Not Detectable Manganese Not Detectable 0.09 ppm Magnesium Not Detectable 7.4 ppm Mercury Not Detectable Not Detectable Nitrate 0.3 ppm 3.95 ppm Potassium 0.03 ppm 26 ppm Selenium Not Detectable Not Detectable Silica Not Detectable Not Detectable Silver Not Detectable Not Detectable Sodium 0.94 ppm 442 ppm Sulfate 2.6 ppm 79 ppm Total Non Not Detectable 575 ppm Volatile Residue Zinc 0.04 4.5

[0047] From the test results above, it is clear that the invention has far less extractable residue than the competitive product. Additionally particulate analysis testing was conducted on a sponge of the preferred embodiment and a conventional sponge. Both the IES-RP-004 biaxial shake test and the IES-RP-004 new zero mechanical stress test were used. These test results are presented in Table 5 and Table 6 below. TABLE 5 (Biaxial Shake Test): Invention Invention Using First Using First Extraction and Second Competitive Process Extraction Sponge Only Processes Number of Particles 338,725 25,301 7026 Released per cm²

[0048] TABLE 4 (New Zero Mechanical Stress Test): Invention Invention Using First Using First Extraction and Second Competitive Process Extraction Sponge Only Processes Number of Particles 37,140 1,462 982 Released per cm²

[0049] The test results above show that the particulate matter released by the invention is substantially lower than that of the competitive device. Therefore, the invention is less likely to damage or contaminate the surface that is to be cleaned. The actual amount of residue after extraction varies somewhat depending on the residue before extraction which is a function of the completeness of reactions during formation of the sponge.

[0050] The extraction processes disclosed above yield a sponge with low extractable residue. By performing both the first and second extraction processes and culling out sponges having residues greater than a desired value for desired elements, a sponge can be made that is particularly suitable for cleaning semiconductor wafers or other materials that must be cleaned very effectively. For example, sponges having 1 ppm or less of zinc and calcium can be selected for cleaning semiconductor wafers. Prior art extraction does not yield a sponge material having such low extractable residues for any starting sponge material. Therefore, the invention provides a sponge that is superior in cleaning semiconductor wafers or the like. Prior art extraction did not attain the low values of extractable residue, particularly zinc and calcium, that are made possible by the invention.

[0051] The disclosed extraction processes can be used to purify other sponge materials, such as that of the competitive product. However, the results may not be as good because the prior art has closed pores and fibrils as noted above. Also, the extraction processes can be applied to sponges rollers that do not have projections or that have different shaped projections. Further, the extraction process and disclosed sponge material can be applied to pads or other cleaning apparatus that are not rollers.

[0052] The invention has been described through a preferred embodiment. However, it will be apparent the various modifications can be made without departing from the scope of the invention as defined by the appended claims. 

What is claimed:
 1. An industrial sponge roller device comprising: a cylindrical body constructed of a polyvinyl acetal material; projections formed of the polyvinyl acetal material and extending from an outer surface of said cylindrical body, said projections being of a truncated conical shape.
 2. An industrial sponge roller device as recited in claim 1, wherein said projections extend from the outer surface by a distance of 0.1875 inches.
 3. An industrial sponge roller device as recited in claim 1, wherein each of said projections has a circular base that is coupled to the outer surface and a circular planar top surface at a free end, a diameter of said base being at least 20% larger than a diameter of said planar surface.
 4. An industrial sponge roller device as recited in claim 3 wherein said top surface has a diameter of 0.25 inches.
 5. An industrial sponge roller device as recited in claim 3, wherein said base has a diameter of 0.31 inches.
 6. An industrial sponge roller device as recited in claim 5 wherein said top surface has a diameter of 0.25 inches.
 7. An industrial sponge roller device as recited in claim 3, wherein an area of said base is substantially 50% larger than an area of said top surface.
 8. An industrial sponge roller device as recited in claim 3, wherein an area of said base is substantially 40% larger than an area of said top surface.
 9. An industrial sponge roller device as recited in claim 1, wherein said projections are arranged in a plurality of rows that extend along an axial direction of said body, adjacent ones of said rows being offset from one another along the axial direction of said body.
 10. An industrial sponge roller device as recited in claim 1, wherein side walls of said projections define an angle in the range of 5-20°, inclusive, with respect to an axis of said projections that is perpendicular to the outer surface.
 11. An industrial sponge roller device as recited in claim 1, wherein axes of adjacent ones of said projections, that extend perpendicular from the outer surface, define an angle of 22.5° with respect to one another.
 12. An industrial sponge roller device as recited in claim 1, wherein said projections cover 35-39%, inclusive, of the outer surface.
 13. An industrial sponge roller device as recited in claim 1, wherein a residual amount of zinc in the polyvinyl acetal material is 2 ppm or less.
 14. An industrial sponge roller device as recited in claim 13, wherein a residual amount of zinc in the polyvinyl acetal material is 1 ppm or less.
 15. An industrial sponge roller device as recited in claim 14, wherein a residual amount of calcium in the polyvinyl acetal material is 2 ppm or less.
 16. An industrial sponge roller device as recited in claim 13, wherein a residual amount of calcium in the polyvinyl acetal material is 1 ppm or less.
 17. An industrial sponge roller device as recited in claim 13, wherein a residual amount of calcium in the polyvinyl acetal material is 2 ppm or less.
 18. An industrial sponge roller device as recited in claim 14, wherein a residual amount of calcium in the polyvinyl acetal material is 1 ppm or less.
 19. An industrial sponge roller device as recited in claim 18, wherein a residual amount of each of arsenic, barium, cadmium, chloride, chromium, copper, iron, lead, manganese, magnesium, mercury, nitrate, potassium, selenium, silica, silver, and sodium is 2 ppm or/less.
 20. An industrial sponge roller device as recited in claim 18, wherein a residual amount of each of arsenic, barium, cadmium, chloride, chromium, copper, iron, lead, manganese, magnesium, mercury, nitrate, potassium, selenium, silica, silver, and sodium is 1 ppm or/less.
 21. A method for extracting residue from an industrial sponge material comprising, in order, the steps of: a) washing and rinsing the material a first time; b) removing all liquid from the material; c) exposing the material to an acid solution; d) washing and rinsing the material a second time; e) exposing the material to an oxidizing solution; and f) washing and rinsing the material a third time.
 22. A method as recited in claim 21, further comprising the steps of: g) washing the material in deionized water; and h) rinsing the material with distilled water.
 23. A method as recited in claim 22, wherein said acid solution is mineral acid at a concentration of 1 to 20% by weight.
 24. A method as recited in claim 22, wherein, during said third working and rinsing step, the pH is raised above 7.0
 25. A method as recited in claim 22, further comprising the steps of: i) washing and rinsing the material a fourth time; j) removing all liquid from the material; k) exposing the material to an acid solution a second time; l) washing and rinsing the material a fifth time; m) exposing the material to an oxidizing solution; and n) repeating steps (i) through (n) until the material contains less than 1.0 ppm HCO equivalent.
 26. A method as recited in claim 25, further comprising the step of: sterilizing the material by irradiating the material with electron beam radiation.
 27. A method as recited in claim 25, wherein said acid solution in step (k) is 0.1 to 10% of a mineral acid.
 28. A method as recited in claim 25, wherein said acid solution in step (k) is 0.2 to 2.0% of a mineral acid.
 29. A method as recited in claim 25, wherein said oxidizing solution in step (m) has a pH of 7.5-11.
 30. A method as recited in claim 25, wherein said oxidizing solution in step (m) has a pH of 8.0-9.5.
 31. A method as recited in claim 25 wherein steps (a)-(n) result in a residual amount of zinc in the industrial sponge material being 2 ppm or less.
 32. A method as recited in claim 25 wherein steps (a)-(n) result in a residual amount of calcium in the industrial sponge material being 2 ppm or less.
 33. A method as recited in claim 25 wherein steps a-n result in a residual amount of zinc in the industrial sponge material being 1 ppm or less.
 34. A method as recited in claim 25 wherein steps a-n result in a residual amount of calcium in the industrial sponge material being 1 ppm or less.
 35. An industrial sponge made by subjecting sponge material to an extracting process for extracting residue, said extracting process comprising, in order, the steps of: a) washing and rinsing the material a first time; b) removing all liquid from the material; c) exposing the material to an acid solution a first time; d) washing and rinsing the material a second time; e) exposing the material to an oxidizing solution; f) washing and rinsing the material a third time; g) washing the material in deionized water; h) rinsing the material with distilled water; i) washing and rinsing the material a fourth time; j) removing all liquid from the material; k) exposing the material to an acid solution a second time; l) washing and rinsing the material a fifth time; m) exposing the material to an oxidizing solution; and n) repeating steps (i) through (n) until the material contains less than 1.0 ppm HCO equivalent.
 36. A sponge as recited in claim 35, wherein said extracting process further comprises the step of: sterilizing the material by irradiating the material with electron beam radiation.
 37. A sponge as recited in claim 35, wherein said acid solution is 0.1 to 10% of a mineral acid.
 38. A sponge as recited in claim 35, wherein said acid solution is 0.2 to 2.0% of a mineral acid.
 39. A sponge as recited in claim 35, wherein said oxidizing solution has a pH of 7.5-11.
 40. A sponge as recited in claim 35, wherein said oxidizing solution has a pH of 8.0-9.5.
 41. A sponge as recited in claim 35, wherein said extracting method further comprises the steps of: (g) washing and rinsing the material in deionized water; and (h) rinsing the material with distilled water.
 42. A sponge as recited in claim 35 having a residual amount of zinc that is 2 ppm or less.
 43. A sponge as recited in claim 35 having a residual amount of calcium that is 2 ppm or less.
 44. A sponge as recited in claim 35 having a residual amount of zinc that is 1 ppm or less.
 45. A sponge as recited in claim 35 having a residual amount of calcium that is 1 ppm or less.
 46. A sponge material as recited in claim 45, wherein a residual amount of each of arsenic, barium, cadmium, chloride, chromium, copper, iron, lead, manganese, magnesium, mercury, nitrate, potassium, selenium, silica, silver, and sodium is 2 ppm or/less.
 47. A sponge material as recited in claim 45, wherein a residual amount of each of arsenic, barium, cadmium, chloride, chromium, copper, iron, lead, manganese, magnesium, mercury, nitrate, potassium, selenium, silica, silver, and sodium is 1 ppm or/less.
 48. An industrial sponge comprising: a body constructed of a polyvinyl acetal material having a residual amount of zinc that is 2 ppm or less.
 49. An industrial sponge comprising: a body constructed of a polyvinyl acetal material having a residual amount of zinc that is 1 ppm or less.
 50. An industrial sponge comprising: a body constructed of a polyvinyl acetal material having a residual amount of calcium that is 1 ppm or less.
 51. An industrial sponge comprising: a body constructed of a polyvinyl acetal material having a residual amount of calcium that is 2 ppm or less.
 52. An industrial sponge device comprising a polyvinyl acetal material having a residual amount of zinc that is 2 ppm or less.
 53. An industrial sponge roller device as recited in claim 50, wherein a residual amount of zinc in the polyvinyl acetal material is 1 ppm or less.
 54. An industrial sponge roller device as recited in claim 52 wherein a residual amount of calcium in the polyvinyl acetal material is 2 ppm or less.
 55. An industrial sponge roller device as recited in claim 52, wherein a residual amount of calcium in the polyvinyl acetal material is 1 ppm or less.
 56. An industrial sponge roller device as recited in claim 49, wherein a residual amount of calcium in the polyvinyl acetal material is 2 ppm or less.
 57. A method of cleaning a silicon material comprising: extracting residue from a polyvinyl acetal sponge material to leave an extractable amount of zinc in the sponge material that is 2 ppm or less; and contacting the silicon material with the sponge material.
 58. A method as recited in claim 57, wherein said extracting step leaves an extractable amount of zinc in the sponge material that is 1 ppm or less.
 59. A method as recited in claim 58, wherein said extracting step leaves an extractable amount of calcium in the sponge material that is 2 ppm or less.
 60. A method as recited in claim 57, wherein said extracting step leaves an extractable amount of calcium in the polyvinyl acetal material that is 1 ppm or less.
 61. A method as recited in claim 57, wherein said extracting step leaves an extractable amount of calcium in the sponge material that is 2 ppm or less.
 62. A method as recited in claim 58, wherein said extracting step leaves an extractable amount of calcium in the sponge material that is 1 ppm or less.
 63. A method as recited in claim 61, wherein said extracting step leaves an extractable amount of each of arsenic, barium, cadmium, chloride, chromium, copper, iron, lead, manganese, magnesium, mercury, nitrate, potassium, selenium, silica, silver, and sodium that is 2 ppm or less.
 64. A method as recited in claim 62, wherein said extracting step leaves an extractable amount of each of arsenic, barium, cadmium, chloride, chromium, copper, iron, lead, manganese, magnesium, mercury, nitrate, potassium, selenium, silica, silver, and sodium that is 1 ppm or less.
 65. A method as recited in claim 63, wherein said extracting step leaves an extractable amount of sulfate that is 10 ppm or less.
 66. A method as recited in claim 64, wherein said extracting step leaves an extractable amount of sulfate that is 10 ppm or less. 